In this study, Bi-Sb-Te thermoelectric materials are produced by mechanical alloying (MA) and spark plasma sintering (SPS). To examine the influence of the milling atmosphere on the microstructure and thermo-electric (TE) properties, a p-type Bi-Sb-Te composite powder is mechanically alloyed in the presence of argon and air atmospheres. The oxygen content increases to 55% when the powder is milled in the air atmosphere, compared with argon. All grains are similar in size and uniformly, distributed in both atmospheric sintered samples. The Seebeck coefficient is higher, while the electrical conductivity is lower in the MA (Air) sample due to a low carrier concentration compared to the MA (Ar) sintered sample. The maximum figure of merit (ZT) is 0.91 and 0.82 at 350 K for the MA (Ar) and MA (Air) sintered samples, respectively. The slight enhancement in the ZT value is due to the decrease in the oxygen content during the MA (Ar) process. Moreover, the combination of mechanical alloying and SPS process shows a higher hardness and density values for the sintered samples.

Citations

Citations to this article as recorded by  

• Advancement of thermoelectric performances through the dispersion of expanded graphene on p-type BiSbTe alloys
  Eun-Ha Go, Rathinam Vasudevan, Babu Madavali, Peyala Dharmaiah, Min-Woo Shin, Sung Ho Song, Soon-Jik Hong
  Powder Metallurgy.2023; 66(5): 722.     CrossRef
• Influence of milling atmosphere on the structure and magnetic properties of mechanically alloyed Fe40Co30Ni30
  Alex Abraham Paul, Anuj Rathi, Ganesh Varma Thotakura, Tanjore V. Jayaraman
  Materials Chemistry and Physics.2021; 258: 123897.     CrossRef
• Enhancement of mechanical properties and thermoelectric performance of spark plasma sintered P-type Bismuth Telluride by powder surface oxide reduction
  Ahmed A. Abdelnabi, Vickram Lakhian, Joseph R. McDermid, Yu-Chih Tseng, James S. Cotton
  Journal of Alloys and Compounds.2021; 858: 157657.     CrossRef
• Solid solution evolution during mechanical alloying in Cu-Nb-Al compounds
  Kaouther Zaara, Mahmoud Chemingui, Virgil Optasanu, Mohamed Khitouni
  International Journal of Minerals, Metallurgy, and Materials.2019; 26(9): 1129.     CrossRef